科研小记 | XRD标准卡片 PDF#00-021-1176

温馨提醒：最好用电脑打开公众号查看

PDF#00-021-1176(RDB)(作废相):质标=空白(B);d=(未知);I=(未知)

Sodium Vanadium Oxide Fluoride Hydrate

Na7 ( V O4 )2 F ·19 H2 O

射线=CuKa1 波长=1.5406 滤波法=

校准= 2θ=10.900-55.368 I/Ic(K值)=

文献: Chretien, Fournier.

Compt. Rend., v266C p1764(1968)

立方晶系-粉末衍射 Z=

晶胞: 14.13x14.13x14.13 <90.0x90.0x90.0> P.S=c??

密度(计算)= 密度(测量)= 分子量=752.09 体积=2821.15 F(29)=3.2(0.146,62/1)

文献: 出处同上

强峰线: 4.06/X 4.96/X 3.14/9 2.71/7 8.11/6 2.46/4 2.87/4 2.23/3

Deleted Or Rejected By: Deleted by 00-027-0693.

Unit Cell Data Source: Powder Diffraction.

   2θ   d(埃)   I(f)  ( h k l)      θ  1/(2d)   2π/d  n^2  

10.900  8.1100   55.0  ( 1 1 1)   5.450  0.0617  0.7747    3

12.581  7.0300   25.0  ( 2 0 0)   6.291  0.0711  0.8938    4

17.869  4.9600   95.0  ( 2 2 0)   8.934  0.1008  1.2668    8

18.947  4.6800   12.0  ( 3 0 0)   9.474  0.1068  1.3426    9

21.874  4.0600  100.0  ( 2 2 2)  10.937  0.1232  1.5476   12

23.643  3.7600    6.0  ( 3 2 1)  11.822  0.1330  1.6711   14

25.354  3.5100   20.0  ( 4 0 0)  12.677  0.1425  1.7901   16

27.507  3.2400   20.0  ( 3 3 1)  13.754  0.1543  1.9393   19

28.401  3.1400   90.0  ( 4 2 0)  14.201  0.1592  2.0010   20

28.966  3.0800   10.0  ( 4 2 1)  14.483  0.1623  2.0400   21

29.756  3.0000   10.0  ( 3 3 2)  14.878  0.1667  2.0944   22

31.138  2.8700   35.0  ( 4 2 2)  15.569  0.1742  2.1893   24

33.027  2.7100   65.0  ( 5 1 1)  16.514  0.1845  2.3185   27

36.496  2.4600   40.0  ( 5 2 2)  18.248  0.2033  2.5541   33

38.439  2.3400   16.0  ( 6 0 0)  19.219  0.2137  2.6851   36

38.801  2.3190    6.0  ( 6 1 0)  19.400  0.2156  2.7094   37

39.856  2.2600    6.0  ( 6 2 0)  19.928  0.2212  2.7802   40

40.510  2.2250   25.0            20.255  0.2247  2.8239    0

42.091  2.1450    6.0  ( 5 3 3)  21.046  0.2331  2.9292   43

43.038  2.1000    6.0  ( 6 3 0)  21.519  0.2381  2.9920   45

43.605  2.0740    6.0  ( 6 3 1)  21.802  0.2411  3.0295   46

46.010  1.9710   20.0  ( 7 1 1)  23.005  0.2537  3.1878   51

46.815  1.9390    6.0  ( 7 2 0)  23.407  0.2579  3.2404   53

47.411  1.9160   10.0  ( 7 2 1)  23.705  0.2610  3.2793   54

48.321  1.8820   20.0  ( 6 4 2)  24.161  0.2657  3.3386   56

48.707  1.8680   20.0  ( 7 2 2)  24.353  0.2677  3.3636   57

49.699  1.8330    6.0  ( 7 3 1)  24.850  0.2728  3.4278   59

51.408  1.7760   10.0  ( 8 0 0)  25.704  0.2815  3.5378   64

53.615  1.7080   10.0  ( 8 2 0)  26.807  0.2927  3.6787   68

55.368  1.6580   10.0  ( 8 3 0)  27.684  0.3016  3.7896   73