PDF#01-080-0377(RDB):质标=星印(S);d=计算值;I=计算值

Nickel Sulfide

Ni S2

射线=CuKa1 波长=1.5406 滤波法=

校准= 2θ=27.695-146.413 I/Ic(K值)=3.21

文献: Fujii, T., Tanaka, K., Marumo, F., Noda, Y.

Mineral. J., v13 p448(1987)

立方晶系-单晶衍射,Pa-3(205) Z=4

晶胞: 5.5745x5.5745x5.5745 <90.0x90.0x90.0> P.S=cP12.00

密度(计算)=4.709 密度(测量)= 分子量=122.82 体积=173.23 F(30)=999.9(0.0001,30/0)

文献: 出处同上

强峰线: 2.79/X 1.68/7 2.49/4 1.97/4 2.28/4 3.22/2 1.07/2 1.49/2

ANX: NO2.

Analysis: Ni1 S2.

Formula from original source: Ni S2.

ICSD Collection Code: 68169.

Pressure of Datacollection: 5400 MPa.

Wyckoff Sequence: c a(PA3-).

Unit Cell Data Source: Single Crystal.

    2θ   d(埃)   I(f)  ( h k l)      θ  1/(2d)   2π/d  n^2  

 27.695  3.2184   20.2  ( 1 1 1)  13.847  0.1554  1.9522    3

 32.087  2.7873  100.0  ( 2 0 0)  16.043  0.1794  2.2543    4

 35.996  2.4930   43.7  ( 2 1 0)  17.998  0.2006  2.5203    5

 39.568  2.2758   39.5  ( 2 1 1)  19.784  0.2197  2.7609    6

 46.013  1.9709   40.3  ( 2 2 0)  23.007  0.2537  3.1880    8

 48.981  1.8582    1.8  ( 2 2 1)  24.491  0.2691  3.3814    9

 54.555  1.6808   66.5  ( 3 1 1)  27.277  0.2975  3.7383   11

 57.198  1.6092   10.9  ( 2 2 2)  28.599  0.3107  3.9045   12

 59.765  1.5461   15.3  ( 0 2 3)  29.882  0.3234  4.0639   13

 62.266  1.4899   18.4  ( 3 2 1)  31.133  0.3356  4.2173   14

 67.108  1.3936    0.1  ( 4 0 0)  33.554  0.3588  4.5085   16

 69.464  1.3520    1.9  ( 4 1 0)  34.732  0.3698  4.6473   17

 71.784  1.3139    1.1  ( 4 1 1)  35.892  0.3805  4.7820   18

 74.072  1.2789    7.8  ( 3 3 1)  37.036  0.3910  4.9130   19

 76.336  1.2465    5.0  ( 0 2 4)  38.168  0.4011  5.0407   20

 78.577  1.2165    4.4  ( 4 2 1)  39.289  0.4110  5.1651   21

 80.801  1.1885    2.0  ( 3 3 2)  40.401  0.4207  5.2867   22

 85.212  1.1379    5.6  ( 4 2 2)  42.606  0.4394  5.5218   24

 87.404  1.1149    0.9  ( 4 3 0)  43.702  0.4485  5.6357   25

 89.593  1.0933    1.2  ( 1 3 4)  44.797  0.4574  5.7473   26

 91.782  1.0728   18.6  ( 5 1 1)  45.891  0.4661  5.8568   27

 96.169  1.0352    5.9  ( 0 2 5)  48.085  0.4830  6.0698   29

 98.375  1.0178    3.2  ( 1 2 5)  49.188  0.4913  6.1735   30

102.828  0.9854    8.1  ( 4 4 0)  51.414  0.5074  6.3760   32

105.083  0.9704    0.6  ( 4 4 1)  52.542  0.5153  6.4749   33

107.362  0.9560    0.3  ( 4 3 3)  53.681  0.5230  6.5722   34

109.670  0.9423    1.3  ( 5 3 1)  54.835  0.5306  6.6682   35

112.011  0.9291    4.8  ( 6 0 0)  56.006  0.5382  6.7628   36

114.392  0.9164    0.7  ( 6 1 0)  57.196  0.5456  6.8561   37

116.818  0.9043    6.0  ( 5 3 2)  58.409  0.5529  6.9481   38

121.839  0.8814    1.5  ( 0 2 6)  60.920  0.5673  7.1286   40

124.453  0.8706    2.2  ( 6 2 1)  62.226  0.5743  7.2172   41

127.151  0.8602    0.6  ( 1 4 5)  63.575  0.5813  7.3046   42

129.949  0.8501    3.5  ( 5 3 3)  64.974  0.5882  7.3911   43

132.867  0.8404    2.0  ( 6 2 2)  66.433  0.5950  7.4765   44

135.929  0.8310    1.7  ( 6 3 0)  67.965  0.6017  7.5610   45

139.172  0.8219    2.1  ( 1 3 6)  69.586  0.6083  7.6446   46

146.413  0.8046    0.1  ( 4 4 4)  73.206  0.6214  7.8090   48